Application: SAM preparation, amine group coating, and hydrophilic surface
Chemical Name: 20-(16-Mercaptohexadecanyloxy)-3,6,9,12,15,18-hexaoxaeicosane-1-amine, hydrochloride

Appearance: White or slightly yellow solid
Purity: ≥95.0% (HPLC)
Solubility:10 mmol/L (Ethyl alcohol, Methyl alcohol, Chloroform)
MW: 574.30, C28H60ClNO6S

Storage Condition: -20oC, protect from light and metal

Shipping Condition: ambient temperature

Structural Formula

Product Description
Polyethyleneglycols (PEGs) are widely used for material modifications to improve hydrophilicity of the surface. PEG-coated materials are usually more stable under physiological conditions. Since Amino-EG6-undecanethiol has 6 ethylene glycol units, 11 carbon atoms, and an SH group at the end, it can be used to prepare a highly oriented and hydrophilic SAM on a gold surface. This is suitable for biomaterial labeling on the surface due to the improved hydrophilicity. The hydrophilic surface can prevent proteins or other biomaterials from non-specific binding. Therefore, the SAM prepared by this reagent will provide a better surface to develop biomaterial sensors or DNA/ protein microarrays. To prepare an Amino-EG6-SAM on a gold surface, hydroxy-EGn-undecanethiols (n=3, 6) are used to dilute the number of amino groups according to the density of the molecules being introduced onto the surface.
How to Prepare SAM
1. Soak a gold-coated glass plate in Piranha solutiona) for 10-15 minutes. Wash the plate with purified water.a)
2. Dissolve aminoalkanethiol compound in ethanol to prepare several mM to several ten mM solutions.
3. Soak the plate in the aminoalkanethiol solution for a certain time period.b)
4. Wash the SAM-coated plate with ethanol and then water.
5. Dry the plate under nitrogen atmosphere, if necessary.
a)Piranha solution: sulfuric acid and 30% hydrogen peroxide, 3:1. Piranha solution is a strong oxidizing agent. Extreme care is necessary when using it.
Do not apply Piranha solution to resin-coated plates; it may erode the resin.
b)To prepare a SAM-coated plate with the best performance, aminoalkanethiol concentration and soaking time should be individually determined.
Application of SAM-Preparation of DNA Array (Fig. 1)
1. Use SF10 glass slides (Schott Glass Technologies) coated with 5 nm chromium and 45 nm gold thin film.
2. Soak the glass slide in a 1 mM 1-octadecanethiol (ODT)/ethanol solution overnight to prepare ODT SAM-coated slide.
3. Draw 500 μm x 500 μm patterns on the ODT SAM-coated slide by UV irradiation with an Hg-Xe arc lamp.a)
4. Soak the slide in a 1 mM 11-amino-1-undecanethiol (AUT)/ethanol solution for 2 hours to form AUT SAM on the 500 μm x 500 μm photopatterned area.
5. Drop 2 mM SPDP solutionb) onto the slide and leave the slide at room temperature.
6. Wash the slide and dry under nitrogen atmosphere.
7. Apply 1 mM thiol-DNA solutionc) to each 500 μm x 500 μm pattern and incubate at room temperature overnight.
8. Incubate the slide with a sample solution for 10 minutes and wash with phosphate buffer, followed by SPR imaging.
a)Irradiation time: 1-1.5 hours
b)SPDP: N-succinimidyl 3-(2-pyridyldithio)propionate. Dissolve SPDP in DMSO to prepare 50 mM solution. Dilute it 25 times with 100 mM triethanolamine buffer, pH 7.0.
c)Dissolve thiol-DNA with 100 mM triethanolamine buffer, pH 8.0.

Fig. 1 DNA Array Preparation Scheme

1. C. Pale-Grosdemange, E. S. Simon, K. L. Prime, and G. M. Whitesides, Anal. Chem., 1999, 71, 777-790.
Item # Description/Size Availability Qty Break Price Quantity
10 mg
8-14 business days 1 $508.00

*Your estimated shipping date is calculated based on production, payment method, destination, and your shipping option.
For Research Use Only Products